Non-standard Automation Commonly Used Materials(Aluminum Component）

Now many people are beginning to understand the non-standard automation, there are many people who have just contact non-standard automation, for these people, we give some relevant explanation, today we talk about non-standard automation of common materials.

AL6061: (magnesium, silicon as the main alloying elements) 55-65 / KG, medium strength <270Mpa, corrosion resistance and machinability.

For heat treatment:

1. nickel plating; 2. anodized HRC42-55 (a: anode color oxidation , Thickness 8-15u; b: anode black oxidation, thickness 20-30u; c: hard anodized, thickness 12-20u; d: hard anodized black, thickness 20-30u).

Click here to learn more about the AL6063 Component: OEM Precision Machining Aluminum Parts

AL6063: (magnesium, silicon as the main alloying elements) 60 / kg, strength <200Mpa.

Click here to learn more about the AL6063 Component: Professional CNC Aluminum Parts

 AL7075: (with zinc as the main alloying elements) 65 / kg, high strength, is 6061 2 times, can be quenched but brittle to the rest of the performance and surface treatment is same with AL6061.

2A12: (copper as the main alloying elements) 35 / kg, the old standard LY12, strength 470Mpa, heat, the production of high-load parts, is the most commonly used hard aluminum alloy.

5A02: (magnesium as the main alloying elements) 35 / kg, the old standard LF2, Japan A5052, a typical rust-resistant alloy, high corrosion resistance, good weldability, high plasticity, strength 245Mpa, making medium load and welding components.